Test Report:Epoxy Resin Silica Microsphere Filler Slurry

2026-03-11

EZHOU ANJEKA TECHNOLOGY CO.,Ltd professional additives manufacturer
Experiment Record Form
Test Name:	Epoxy Resin Silica Microsphere Filler Slurry					Temperature/Humidity:
Client:		Applicant:	Mr Yang	Test Date:	February 26, 2026
Objective: Testing viscosity reduction, defoaming, and anti-settling properties of filler slurry for epoxy potting compounds
Pigment Paste Formulation 40 692 1.2 Dispersant 0.2 6912, 6910A, 6911A Defoamer 0.2 5680A, 5088 Anti-settling Agent 0.2 6710, 4410S Silica Microsphere 60 Customer
128 Resin	40	Customer
692	1.2	Customer
Dispersant	0.2	6912,6910A,6911A
Defoamer	0.2	5680A,5088
Anti-settling Agent	0.2	6710,4410S
Silica Microsphere	60	Customer
Experimental Method
High-speed stirring at 2000 rpm for 15 minutes for comparison.
Test Results Test 6710 4410S 6912 6910A 6911A 6912 6910A 6911A 382123 179552 276233 244006 110493 138117 178266 375217 377519 379821 195665 Gloss 20°:22.2 60°:93.8 20°: 66.4 60°: 99.4 20°: 38.5 60°：83.1 20°: 16.2 60°: 92.6 20°: 38.9 60°：90.7 20°: 43.5 60°：89.5 20°: 42.2 60°: 92 Anti-settling Soft sedimentation No sedimentation No sedimentation No sedimentation Soft sedimentation No sedimentation Soft sedimentation
Test	Blank	6710			4410S
Test	Blank	6912	6910A	6911A	6912	6910A	6911A
Pre-Heat Storage Viscosity	382123	179552	276233	244006	110493	138117	178266
Viscosity after 1 day thermal storage		375217	377519	379821		195665
Gloss	20°:22.2 60°:93.8	20°: 66.4 60°: 99.4	20°: 38.5 60°：83.1	20°: 16.2 60°: 92.6	20°: 38.9 60°：90.7	20°: 43.5 60°：89.5	20°: 42.2 60°: 92
Anti-settling	Soft sedimentation	No sedimentation	No sedimentation	No sedimentation	Soft sedimentation	No sedimentation	Soft sedimentation
Defoaming: 6910A demonstrated the best defoaming effect in 4410S, with minimal bubbles around the cup and no surface bubbles. Testing 4410S 5088 5680A 6910A(0.2%) 6910A(0.4%) 6910A (0.4%) Viscosity before thermal storage 225591 250912 262422 Viscosity after 1 day thermal storage 264724 375279 271779 Gloss 20°: 58.4 60°：98.5 20°: 70.8 60°：99.1 20°: 60 60°: 93.7 Settling No sediment No sediment No sediment Defoaming Minimal bubbles around cup, no surface bubbles Surface bubbles present
Test	4410S
	5088		5680A
	6910A(0.2%)	6910A(0.4%)	6910A(0.4%)
Viscosity before thermal storage	225591	250912	262422
Viscosity after 1 day thermal storage	264724	375279	271779
Gloss	20°: 58.4 60°：98.5	20°: 70.8 60°：99.1	20°: 60 60°: 93.7
Anti-settling	No sedimentation	No sedimentation	No sedimentation
Defoaming	Minimal bubbles around the cup, no surface bubbles		Surface bubbles present
Conclusion
The best results were achieved using 4410S as the anti-settling agent, 6910A as the dispersant, and 5088 as the defoamer.

Εκδηλώσεις

Ειδήσεις

Υποθέσεις

Επαφές

Επαφές: Ms. Anna

Τηλεφώνημα: 86-0711-5117111

Φαξ: 86-0711-3809626

Επικοινωνήστε τώρα

Μας ταχυδρομήστε

Πολυμερές διασκορπιστικό παράγοντα

Διασκορπιστής χρωστικών

Διασκορπισμός νανοσωματιδίων

Αντιμετώπιση διασκορπισμού βαφής

Ενυδατικός και διασκορπιστικός παράγοντας

Διασκορπιστικό χρωστικής ουσίας που μεταφέρεται στο νερό

Ονομαστικός παράγοντας

Αντικατασταλτικός παράγοντας

Θικσοτροπικός παράγοντας

αποσφενωτικό

Προωθητής προσκόλλησης

Διασκορπιστικό γενικής χρήσης

Πρόσθετα χρώματα με βάση το νερό

Πρόσθετα χρώματα με βάση το λάδι

Διασκορπισμός κεριού από πολυαιθυλένιο

Συγκεντρωμένο εναιώρημα

Πολυμερές διασκορπιστικό παράγοντα

Διασκορπιστής χρωστικών

Διασκορπισμός νανοσωματιδίων

Αντιμετώπιση διασκορπισμού βαφής

Ενυδατικός και διασκορπιστικός παράγοντας

Διασκορπιστικό χρωστικής ουσίας που μεταφέρεται στο νερό

Ονομαστικός παράγοντας

Αντικατασταλτικός παράγοντας

Θικσοτροπικός παράγοντας

αποσφενωτικό

Προωθητής προσκόλλησης

Διασκορπιστικό γενικής χρήσης

Πρόσθετα χρώματα με βάση το νερό

Πρόσθετα χρώματα με βάση το λάδι

Διασκορπισμός κεριού από πολυαιθυλένιο

Συγκεντρωμένο εναιώρημα

Test Report:Epoxy Resin Silica Microsphere Filler Slurry

Ειδήσεις

Υποθέσεις

Πολυμερές διασκορπιστικό παράγοντα

Διασκορπιστής χρωστικών

Διασκορπισμός νανοσωματιδίων

Αντιμετώπιση διασκορπισμού βαφής

Ενυδατικός και διασκορπιστικός παράγοντας

Διασκορπιστικό χρωστικής ουσίας που μεταφέρεται στο νερό